Medical Devices Zinc Rich Epoxy Primer Powder Coating RAL 1007 Color

Medical Devices Zinc Rich Epoxy Primer Powder Coating RAL 1007 Color

  • High Light

    inorganic zinc primer coating

    ,

    anti corrosive epoxy primer

  • Color
    Daffodil Yellow
  • Substrate
    Fitness Equipment
  • Surface Type
    Silk
  • Package
    Carton
  • State
    Overcoated
  • Origin
    Ukraine
  • Place of Origin
    Ukraine
  • Brand Name
    TOPO
  • Certification
    CE, BV, ROHS
  • Model Number
    ZR-RAL1007
  • Minimum Order Quantity
    Negotiable
  • Price
    Negotiable
  • Packaging Details
    Two-ply PVC bag inside with carton box, net weight 20/25kg
  • Delivery Time
    7 days
  • Payment Terms
    L/C, T/T, Western Union, MoneyGram
  • Supply Ability
    400 T/Month

Medical Devices Zinc Rich Epoxy Primer Powder Coating RAL 1007 Color

RAL1007 daffodil yellow Organic  zinc rich epoxy primer for Medical Devices

 

ADVANTAGES

  • Meets SSPC Paint Specification no. 20, Type II.
  • Meets ASTM D 520 Type I
  • Bonds tenaciously to metal.
  • Promotes adhesion of subsequent coats.

Steel surfaces should be abrasive blasted to a commercial gray metal finish as specified by the Steel Structures Painting Council SSPC SP-6.

 

PHYSICAL PROPERTIES
Color Gray
Solids 58% by volume
Solids 88% by weight
Total zinc dust by weight of solids 90%
Finish Flat
Viscosity 100 Krebs units
VOC 2.95 lbs / gallon
Dry Temperature Resistance Without Topcoating. Continuous 300 degrees F
Intermittent 400 degrees F

 

 

POWDER AND COATING PROPERTIES

  • Specific gravity : 2.0 - 2.2
  • Film thickness (ISO 2178) : 60 - 90 μm
  • Flow out : Good
  • Gloss (ISO 2813, 60º) : 50-60 %
  • Adhesion (ISO 2409) : GT= 0
  • Pencil hardness(ASTM D3363 ) : 2H
  • Direct and reverse impact (ASTM D2794) : >50kg.cm
  • Salt spray Resistance ( ASTM B117, 2000hrs)
  • (Maximum undercutting ,2 mm ): No blistering
  • Chemical Resistance : Generally excellent resistance to dilute acids, alkalis, oil and most solvents at normal temperatures

   

Zinc epoxy with zinc silicate properties
New binder technology shows superior performance in adhesion/cohesion and electrical conductivity between the zinc particles and the steel compared to traditional zinc rich epoxy coatings.

 

Test Item

Test Method

Test Result

Film Thickness

ISO2360

60-80um

Pencil Hardness

ASTMD 3363

HB-H

Bending

ISO1519

≤10mm

Grid Test 1mm

ISO2409

0 Class

Impulse Test

ASTMD2794

Pass

Cupping Test

ISO1520

≥8mm

Heat Resistance 1000 hours

ISO6270-1

Popping<1mm

Salt Spray 1000 hours

ISO9227

Corrosion Spreading<1mm

 

 

 