Durable Corrosion Resistant Coatings , RAL 1007 Aerospace Powder Coating
-
High Light
steel corrosion protection coatings
,protective powder coating
-
ColorDaffodil Yellow
-
ComponentsResin, Pigment
-
AppearanceFine Powder
-
Adhesion0 Grade
-
PackingCarton
-
Curing180-200ºC,10 Min-15 Min
-
Place of OriginUkraine
-
Brand NameTOPO
-
CertificationCE, BV, ROHS
-
Model NumberAC-RAL1007
-
Minimum Order QuantityNegotiable
-
PriceNegotiable
-
Packaging DetailsTwo-ply PVC bag inside with carton box, net weight 20/25kg
-
Delivery Time7 days
-
Payment TermsWestern Union, MoneyGram, L/C, T/T
-
Supply Ability400 T/Month
Durable Corrosion Resistant Coatings , RAL 1007 Aerospace Powder Coating
RAL1007 daffodil yellow Anti Corrision powder coating for Electrical Household Appliances
It is specifically designed for meeting the requirement of super anti-coccosive property.
Its outstanding gloss retention, durable color stability and mechanical properties make it best to be applied to construction materials, oil pipelines, boats, electrical appliances, metal furnitures, decorations...
Compared with liquid paint, powder coating is more environmental friendly and economic. It can form a harder & thicker finish. Its excellent properties and attractive appearance of this product make it suitable for application to any other metal substrates.
| Property | Standard | Result |
| Film appearance & color | No unevenness and no color difference | |
| Adhesion | EN ISO 2409 (2mm) | Cross-cut rating Gt0 (100% adhesion) |
| Impact resistance | EN ISO 6272/ASTM D2794 | 50Kg/cm² without film cracking |
| Cupping test | EN ISO 1520 | Indentation depth in excess of 5mm without film cracking |
| Flexibility | EN ISO 1519 | Cylindrical Mandrel bending test, passes 2 mm |
| Film hardness | EN ISO 2815 | 1H - 2H by Pencil Hardness Test |
| Drilling, milling and sawing | No flaking of coating | |
| Neutral salt spray resistance | ASTM B117 | No blistering or loss of adhesion after 1000 hours |
| Humidity resistance containing SO2 | EN ISO 3231 | No infiltration exceeding 1 mm on both sides of the scratch after 30 cycles. |
| Humidity resistance | EN ISO 270-2 |
No infiltration exceeding 1 mm on both sides of the scratch after 1000 hours. |
| Acetic acid salt spray resistance | ISO 9227 | After 1000 hours testing - maximum 16mm infiltration over a scratch length of 10cm |
| Accelerated weathering | DIN EN ISO 11507 (UVB - 313) |
Cycle: 4 hours at 50 C UV and 4 hours at 40 C condensation. No chalking, excellent gloss retention and color stability after 300 hours testing. |
| Accelerated weathering | DIN EN ISO 11507 (UVA - 340) |
Cycle: 8 hours at 60 C UV and 4 hours at 45 C condensation. No chalking, excellent gloss retention and color stability after 1000 hours testing. |
| Natural weathering test | ISO 2810 | No chalking, excellent gloss retention and color stability after 12 months exposure (angle of 5° to South). |
Our products are sold all over the world, you can rest assured.